410 Stainless Steel

 

 

410 stainless steel is a basic martensitic grade offering both exceptional wear and corrosion resistance. Elevated mechanical properties and corrosion resistance are achieved with stainless steel 410 when it's hardened and tempered. 410 stainless steel is used in applications such as dental and surgical instruments, pipelines, valves and nozzles, automotive parts and more.

 

 

Standards

 UNS S41000

 ASTM A182

 ASTM A276

 ASTM A479

Composition(%)

Carbon 0.080-0.150

Chromium 11.50-13.50

Manganese 1.0 Max

Phosphorus 1.0 Max

Silicon 1.00 Max

Sulfur 0.030 Max

 

 

Round bar steel: 1mm to 1500mm diamter
Plate steel:0.1mm to 40mm
Width: 10mm to 2500mm
Length: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubes: OD: 3-1200mm, with wall thickness ranging from 0.5-55 mm.

 

 

410 Stainless Steel (annealed condition)
Minimum Properties	Ultimate Tensile Strength, psi	65,000
	Yield Strength, psi	30,000
	Elongation	20 - 34%
	Rockwell Hardness	B82
Chemistry	Iron (Fe)	86%
	Carbon (C)	0.15% max
	Chrome (Cr)	12.5%
	Manganese (Mn)	1% max
	Phosphorus (P)	0.04% max
	Sulphur (S)	0.03%

 

  Type 410 is used for springs, scrapers, fasteners, hardware brackets, furnace parts and burners. It is magnetic in all conditions. Tensile strength (as annealed) min. 65,000 PSI, yield strength minimum 30,000 PSI, and elongation in 2 inches at 20%. For solution annealing, slow controlled cooling from 1500/1600 F. For hardening, heat to 1700/1850 F. Quench in air or oil.