UNS N07520
UNS N07520
Bar
|
Element |
Minimum (weight %) |
Maximum (weight %) |
|
W |
1.0 | |
|
Ti |
3.0 | |
|
Mo |
6.0 | |
|
Cr |
19.0 | |
|
Co |
12.0 | |
|
C |
0.05 | |
|
B |
0.007 | |
|
Al |
2.0 | |
|
Ni |
Balance | |
Density
|
lb/in3 |
g/cm3 |
|
0.297 |
8.22 |
Tensile Strength
|
ksi |
MPa |
|
190 min |
1,310 min |
Yield Strength
|
ksi |
MPa |
|
120 min |
828 min |
Hardness
|
40 HRC |
Elongation
|
20% min |